Method for producing glass for display substrate

ABSTRACT

A method of producing a glass having a SiO 2 —Al 2 O 3 —B 2 O 3 —RO based composition, where RO is at least one of MgO, CaO, BaO, SrO and ZnO, a melting temperature corresponding to 10 2.5  poise of 1570° C. or higher and an alkali content of 0.01 to 0.2% and a ZrO 2  content of 0.01 to 0.3%, as expressed in % by mass. And, a method of producing a glass having a SiO 2 —Al 2 O 3 —B 2 O 3 —RO based composition, where RO is at least one of MgO, CaO, BaO, SrO and ZnO, a density of 2.5 g/cm 3  or less, an average thermal expansion coefficient of 25 to 36×10 −7 /° C. in a temperature range of 30 to 380° C., a strain point of 640° C. or higher and an alkali content of 0.01 to 0.2% and a ZrO 2  content of not less than 0.01% and less than 0.4%, as expressed in % by mass.

This application is a division of application Ser. No. 11/083,937 filedMar. 21, 2005, which claims priority based on Japanese PatentApplication Nos. 2004-82415 and 2005-22809, filed Mar. 22, 2004, andJan. 31, 2005, respectively, and which are incorporated herein byreference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a glass for a substrate which is usedin a flat display substrate such as a liquid crystal display and an ELdisplay.

2. Description of the Related Art

An alkali-free glass substrate has been widely used as a flat displaysubstrate such as a liquid crystal display and an EL display.

In particular, since an electron device such as a thin filmtransistor-type active matrix liquid crystal display (TFT-LCD) is athin-type and has a small consumption power, the device has been used invarious utilities such as car navigation and a finder of a digitalcamera and, in recent years, a monitor of a personal computer and a TV.

In a TFT-LCD panel maker, improvement in productivity and cost reductionare tried by manufacturing plural devices on a glass substrate, whichformed by a glass maker, and dividing into every device to obtain aproduct. In recent years, in utilities such as a monitor of a personalcomputer or a TV, a large size has been required in a device itself and,in order to produce a plurality of such kind of large devices at onetime, therefore a glass substrate having a large area such as 1000×1200mm has been required.

In addition, in a portable-type device such as a cellular phone and anote-type personal computer, for convenience for carrying, weightreduction of an instrument is required, and weight reduction is alsorequired in a glass substrate. In order to reduce a weight of a glasssubstrate, thickness reduction of a substrate is effective and,currently, a standard thickness of a glass substrate for TFT-LCD is verythin such as about 0.7 mm.

However, the aforementioned large-sized thin glass substrate has greatsag due to a self-weight, and this has become a great problem in amanufacturing step.

That is, this kind of a glass substrate is formed by a glass maker, andpassed through steps such as cutting, annealing, inspection and washing.During these steps, the glass substrate is placed into or taken out froma cassette in which a multiple-staged shelf is formed. This cassette canhold glass substrates in a horizontal direction such that both sides orthree sides of the glass substrate are supported only by shelves formedon left and right inside walls, or left, right and back inside walls.However, since a large-sized thin glass substrate has a large amount ofsag, when a glass substrate is placed into a cassette, a part of theglass substrate is contacted with the cassette or another glasssubstrate leading to breakage, or when the glass substrate is taken outfrom the cassette, it is greatly rocked, easily leading to unstability.On the other hand, in a display maker, since the same form of thecassette is used, the similar, problem arises.

A sag amount due to a self-weight of such the glass substrate varies inproportion to a glass density and in inverse proportion to a Young'smodulus. Accordingly, in order to suppress a sag amount of a glasssubstrate small, it is necessary that a specific Young's modulusexpressed by a ratio of Young's modulus/density is increased. In orderto increase a specific Young's modulus, a glass material having a highYoung's modulus and a low density becomes necessary and, at the samespecific Young's modulus, in a glass having a lower density, a thicknessof a glass sheet having the same weight can be increased by a portion ofa reduced weight. Since a sag amount of a glass varies in reverseproportion to a square of a sheet thickness, effect of reducing sagderived from increase in a sheet thickness is very great. Sincereduction in a glass density has great effect also on weight reductionof a glass, the glass having as smaller as possible density is better.

Generally, this kind of an alkali-free glass contains a relatively largeamount of an alkaline earth metal oxide. In order to reduce a density ofthe glass, it is effective to reduce a content of the alkaline earthmetal oxide. However, since the alkaline earth metal oxide is acomponent which promotes meltability of a glass, meltability is reducedwhen the content is decreased. When meltability of a glass is reduced,internal defects such as seeds and stones easily occur in the glass.Since seeds and stones in a glass prevent transmission of light, thisbecomes a fatal defect to the glass substrate for display. In order tosuppress such the internal defects, a glass must be melted at a hightemperature for a long period of time. On the other hand, melting at ahigh temperature increases a burden on a glass melting furnace. Arefractory used in the furnace is more eroded at a higher temperature,and a life cycle of the furnace becomes shorter.

In addition, in this kind of a glass substrate, thermal shock resistanceis also an important requirement. A fine flaw and crack are present onan end face of a glass substrate even when chamfered and, when a tensilestress due to heat is exerted by concentrating on the flaw and thecrack, the glass substrate is broken in some cases. Breakage of a glasssubstrate not only decreases an operation rate, but also a fine glasspowder produced upon breakage is adhered on other glass substrates, andthis causes disconnection and deteriorated patterning, thus, there is apossibility that manufacturing circumstances are contaminated.

Meanwhile, as a recent direction of development of TFT-LCD, in additionto increase in a size of a screen and weight reduction, increase inperformance such as a higher definition, a higher speed response and ahigher aperture ratio is exemplified. In particular, in recent years,for the purpose of increase in performance and weight reduction of aliquid crystal display, polycrystalline silicon TFT-LCD (p-Si.TFT-LCD)has been extensively developed. In the previous p-Si.TFT-LCD, since atemperature at its manufacturing step is very high such as 800° C. orhigher, only a quartz glass substrate could be used. However, by recentdevelopment, a temperature at a manufacturing step is lowered to 400 to600° C., and an alkali-free glass substrate has become to be used as inamorphous silicon TFT-LCD (a-Si.TFT-LCD) which is currently produced ata large scale.

In a step of manufacturing p-Si.TFT-LCD, since there is manyheat-treating steps and a glass substrate is repeatedly heated rapidlyand cooled rapidly as compared with a step of manufacturinga-Si.TFT-LCD, thermal shock on the glass substrate is further increased.Further, a size of a glass substrate is increased as described above,not only there easily arises a difference in a temperature of the glasssubstrate, but also a possibility that fine flaws and cracks areproduced on an end face is also increased. Therefore a possibility thatthe substrate is broken during a heating step is increased. The mostfundamental and effective method for solving this problem is to reduce athermal stress generated from a difference in thermal expansion and, forthis reason, a glass having a low thermal expansion coefficient isrequired. In addition, since when a difference in thermal expansionbetween a thin film transistor (TFT) material and glass becomes great,warpage occurs in the glass substrate, it is also required to have athermal expansion coefficient approximate to that (about 30 to 33×10⁻⁷°C.) of a TFT material such as p-Si.

In addition, it is said that a temperature at a step of manufacturingp-Si.TFT-LCD has been lowered recently, but the temperature is stillsignificantly higher as compared with a temperature at a step ofmanufacturing a-Si.TFT-LCD. If a glass substrate has a low heatresistance, when the glass substrate is exposed to a high temperature of400 to 600° C. during the step of manufacturing p-Si.TFT-LCD, finedimensional shrinkage called thermal compaction is caused, and thiscauses variance of a pixel pitch of TFT, and this may be a cause fordeteriorated display. In addition, if a glass substrate has a furtherlower heat resistance, there is a possibility that deformation andwarpage of the glass substrate are caused. Further, also in order toprevent occurrence of pattern shift by thermal compaction of a glasssubstrate at a step of manufacturing a LCD such as film deposition step,the glass excellent in heat resistance is required.

Further, on a surface of a glass substrate for TFT-LCD, a transparentelectrically conductive film, an insulating film, a semiconductor filmand a metal film are formed and, moreover, various circuits and patternsare formed by photolithography etching (photoetching). In addition, inthese film formation and photoetching step, the glass substrate issubjected to various heat treatment and chemical treatment.

Therefore, when an alkali metal oxide (Na₂O, K₂O, Li₂O) is contained ina glass, it is thought that an alkali ion is diffused into a formedsemiconductor substance film during heat treatment, leading todeterioration of film property, and it is required that an alkali metaloxide is not substantially contained. Further, it is required that suchthe chemical resistance is possessed that deterioration is not caused bychemicals such as various acids and alkalis used in a photoetching step.

In addition, a glass substrate for TFT-LCD is formed mainly by adown-draw process or a float process. Examples of a down-draw processinclude a slot down-draw process and an overflow down-draw process and,since a glass substrate formed by the down-draw process does not needpolishing process, there is an advantage that cost reduction is easy.However, when a glass substrate is formed by a down-draw process, sincethe glass is easily devitrified, the glass excellent in devitrificationresistance is required.

Then, an alkali-free glass for a substrate characterized in that theaforementioned various properties are satisfied and, in particular, alow density, low expansion, and a high strain point are possessed isproposed (e.g. Japan Unexamined Patent Publication JP-A No.2002-308643).

The alkali-free glass having a low density, low expansion and a highstrain point disclosed in JP-A No. 2002-308643 has a density of 2.45g/cm³ or a lower, an average thermal expansion coefficient in atemperature range of 30 to 380° C. of 25 to 36×10⁻⁷/° C., and a strainpoint of 640° C. or higher, thus, the aforementioned requirements aresatisfied. However, the aforementioned alkali-free glass has a meltingtemperature (temperature corresponding to 10^(2.5) poise) ofapproximately 1580° C. or higher, and high temperature melting isnecessary.

Then, electric melting is frequently applied to high temperature meltingof such the glass. In the case of electric melting, a glass meltingfurnace is usually constructed of an alumina electrocast refractoryhaving a high electric resistance. However, the alumina electrocastrefractory is easily eroded by glass melt as compared with, for example,a high zirconia refractory, and has a short life. In particular, when analumina electrocast refractory is used in a furnace for melting a glassrequiring the aforementioned high temperature melting, the refractory iseroded in a short period of time, and stable operation can not beperformed over a long period of time. As a result, a melting furnacemust be frequently repaired, productivity is reduced, and a facilitycost is increased. In addition, when an alumina electrocast is used,lots of seeds are generated from the refractory.

Under such the circumstances, use of an electric melting furnace using ahigh zirconia refractory having erosion resistance and hardly generatingseeds is being studied. However, when the aforementioned glass having alow density, low expansion, and a high strain point is electricallymelted in a melting furnace using a high zirconia refractory, therearises a problem that the glass is easily devitrified in a later formingstep.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a glass for a displaysubstrate which has a low density, low expansion and a high strainpoint, and hardly causes devitrification at forming even whenelectrically melted in a melting furnace constructed of a high zirconiarefractory, and a process for preparing the same.

A glass for a display substrate of the present invention ischaracterized in that the glass has a SiO₂—Al₂O₃—B₂O₃—RO (RO is at leastone of MgO, CaO, BaO, SrO and ZnO) based composition, a temperaturecorresponding to 10^(2.5) poise is 1570° C. or higher, preferably 1580°C. or higher and, expressed in % by mass, a content of an alkali is 0.01to 0.2%, and a content of ZrO₂ is not less than 0.01% and less than0.4%.

In addition, a glass for a display substrate of the present invention ischaracterized in that the glass has the SiO₂—Al₂O₃—B₂O₃—RO (RO is atleast one of MgO, CaO, BaO, SrO and ZnO) based composition, a density is2.5 g/cm³ or less, an average thermal expansion coefficient in atemperature range of 30 to 380° C. is 25 to 36×10⁻⁷/° C., a strain point640° C. or higher and, expressed in % by mass, a content of an alkali is0.01 to 0.2%, and a content of ZrO₂ is not less than 0.01% and less than0.4%.

In addition, in the glass for a display substrate of the presentinvention, the content of ZrO₂ expressed in % by mass is preferably 0.01to 0.3%, and an alkali component is preferably such that, expressed in %by mass, 0.007 to 0.2% of Na₂O, 0 to 0.05% of Li₂O, and 0 to 0.05% ofK₂O are contained.

In addition, in the glass for display substrate of the presentinvention, it is preferable that a β-OH value of the glass is 0.20/mm ormore.

In addition, in the glass for a display substrate of the presentinvention, it is preferable that, expressed in % by mass, 50 to 70% ofSiO₂, 10 to 25% of Al₂O₃, 8.4 to 20% of B₂O₃, 0 to 10% of MgO, 6 to 15%of CaO, 0 to 10% of BaO, 0 to 10% of SrO, 0 to 10% of ZnO, 0 to 5% ofTiO₂, and 0 to 5% of P₂O₅ are contained.

In addition, it is preferable that the glass for a display substrate ofthe present invention is 0.1 m² or more in area.

In addition, it is preferable that the glass for a display substrate ofthe present invention is used as a liquid crystal display substrate oran EL display substrate.

A method of using a glass for a display substrate of the presentinvention is characterized in that the glass for a display substrate isused as a substrate for a liquid crystal display or an EL display.

A method for producing a glass for a display substrate of the presentinvention is a method for producing a glass for a display substrate byelectrically melting glass raw materials mixed so that the glass havinga SiO₂—Al₂O₃—B₂O₃—RO (RO is at least one of MgO, CaO, BaO, SrO and ZnO)based composition and having a temperature corresponding to 10^(2.5)poise of 1580° C. or higher is obtained, in a melting furnaceconstructed of a high zirconia refractory, and refining, homogenizingand forming the melt, characterized in that the glass raw materials aremixed so that a content of an alkali of the resulting glass is 0.01 to0.2% as expressed in % by mass.

In addition, a method for producing a glass for a display substrate ofthe present invention is a method for producing a glass for a displaysubstrate by electrically melting glass raw materials mixed so that theglass having a SiO₂—Al₂O₃—B₂O₃—RO (RO is at least one of MgO, CaO, BaO,SrO and ZnO) based composition, a density of 2.5 g/cm³ or less, anaverage thermal expansion coefficient in a temperature range of 30 to380° C. of 25 to 36×10⁻⁷/° C., and a strain point of 640° C. or higheris obtained, in a melting furnace constructed of a high zirconiarefractory, and refining, homogenizing and forming the melt,characterized in that the glass raw materials are mixed so that acontent of an alkali of the obtained glass is 0.01 to 0.2% as expressedin % by mass.

In addition, in the method for producing a glass for a display substrateof the present invention, it is preferable that the glass raw materialsare mixed so that an alkali component is 0.007 to 0.2% of Na₂O, 0 to0.05% of Li₂O, and 0 to 0.05% of K₂O as expressed in % by mass.

In addition, in the method for producing a glass for a display substrateof the present invention, it is preferable that a β-OH value of theresultant glass is 0.20/mm or more.

In addition, in the method for producing a glass for a display substrateof the present invention, it is preferable that a content of ZrO₂ of theresultant glass is not less than 0.01% and less than 0.4%, particularly0.01 to 0.3% as expressed in % by mass.

In addition, the method for producing a glass for a display substrate ofthe present invention, it is preferable that the raw materials are mixedso that the glass comprising 50 to 70% of SiO₂, 10 to 25% of Al₂O₃, 8.4to 20% of B₂O₃, 0 to 10% of MgO, 6 to 15% of CaO, 0 to 10% of BaO, 0 to10% of SrO, 0 to 10% of ZnO, 0 to 5% of TiO₂, and 0 to 5% of P₂O₅ isobtained.

In addition, it is preferable that the glass for a display substrate ofthe present invention is prepared by the aforementioned process.

Since even when the glass for a display substrate of the presentinvention is electrically melted in a melting furnace constructed of ahigh zirconia refractory from necessity of high, temperature melting,erosion of the refractory is little, the glass is hardly devitrified.Moreover, the glass has a low density, low expansion, and a high strainpoint, is small in a thermal compaction amount or a sag amount, isexcellent in thermal shock resistance, and has warpage which is hardlyoccurred. For this reason, the glass is suitable as a glass for a liquidcrystal display substrate.

In addition, according to the present method, although high temperaturemelting is necessary, a glass having no seed and no devitrification, andhaving a low density, low expansion and a high strain point can beproduced without repairing a melting furnace for a long term, and theglass of high quality can be provided at a low cost.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

According to research by the present inventors, a high zirconiarefractory has a lower volume resistivity than that of the glass havinga low density, low expansion and a high strain point, a representativeof which is described in the above JP-A reference, in a meltingtemperature region of the glass. For this reason, when theaforementioned glass is electrically melted in an electric meltingfurnace constructed of the high zirconia refractory, a current is flownthrough not only the molten glass but also the refractory. As a result,the high zirconia refractory is eroded, and a concentration of ZrO₂ inthe glass is increased, and it is presumed that this is a cause fordevitrification at forming.

Then, in the present invention, the aforementioned problem is solved bydaring addition of an alkali component which has been previouslyprohibited to be contained in utilities of, in particular, a liquidcrystal display, in a glass having a temperature corresponding to10^(2.5) poise of 1570° C. or higher, particularly 1580° C. or higherwhich needs high temperature melting, for the purpose of reducing avolume resistivity of the glass in a melting temperature region.

Specifically, the glass contains an alkali component (one or more kindsof Li₂O, Na₂O and K₂O) at 0.01% or more, preferably 0.02% or more,further preferably 0.05% or more as expressed in % by mass. The upperlimit is 0.2% by mass or less, preferably 0.1% by mass or less. It isthought that, by addition of a prescribed amount of an alkali component,a volume resistivity of the glass melt is reduced, a current easilypasses through the glass melt during electric melting, and the currentpasses through the high zirconia refractory side with relativedifficulty. As a result, erosion of the refractory is suppressed, anddevitrification of the glass is improved. On the other hand, when thealkali component exceeds 0.2%, various properties of a film formed onthe substrate are deteriorated due to diffusion of the alkali ion causedby heat treatment. In addition, there is a possibility that chemicaldurability of the resultant glass is reduced. In the present invention,the content of the alkali is very small, and reduction in the volumeresistivity in a high temperature region caused by addition of thealkali is slight. However, this slight reduction in the volumeresistivity influences on easiness of flow of the current into the highzirconia refractory, and it becomes possible to considerably reduce theerosion amount from the refractory. It is preferable that the amount ofNa₂O, among the alkali component, is the largest. In addition, it ispreferable that the content of Na₂O alone is 0.007% or more,particularly 0.01% or more, and further 0.02% or more, and it isdesirable that the content is 0.2% or less, 0.15% or less, particularly0.08% or less. Although not essential regarding other alkali components,it is preferable that a content of Li₂O is 0.0001% or more, particularly0.0007% or more, further 0.001% or more, and it is desirable that thecontent is 0.05% or less, particularly 0.02% or less. In addition, it ispreferable that a content of K₂O is 0.0001% or more, particularly 0.001%or more, further 0.003% or more, and it is desirable that the content of0.05% or less, particularly 0.02% or less.

In addition, the glass for a display substrate of the present inventioncontains 0.01% or more, preferably 0.02% or more of ZrO₂ as expressed in% by mass. Its upper limit is less than 0.4%, preferably 0.3% or less,more preferably 0.2% or less, further preferably 0.1% or less. When thecontent of ZrO₂ is 0.4% or more, the glass is easily devitrified. Thistendency is remarkably manifested, particularly in a composition rangeof the present invention described later. In addition, also when SnO₂ iscontained in the glass, tendency of devitrification of the glass due toZrO₂ becomes strong. Like this, from a viewpoint of improvement indevitrification, a smaller amount of ZrO₂ is better. However, reductionin chemical durability due to addition of an alkali component is feared.In addition, it is not preferable to completely exclude ZrO₂ as animpurity from glass raw materials or a cullet since a raw material costis increased. In addition, since the high zirconia refractory is used ina melting step, it is difficult to completely prevent the refractoryfrom dissolving into the glass melt. Then, in the present invention, thelower limit value of ZrO₂ is set at 0.01%. By containing ZrO₂ at 0.01%or more, chemical durability of the glass can be expected to beimproved. In addition, regarding ZrO₂, it is not necessary to use a rawmaterial having an excessively high purity, and it becomes possible toavoid increase in a raw material cost.

In addition, in a glass requiring high temperature melting, even smallreduction in a viscosity leads to improvement in meltability. Forreducing the viscosity at high temperature, it is effective to increasemoisture in the glass. Then, in the substrate glass of the presentinvention, it is preferable that the moisture amount of the glass asexpressed by a β-OH value is 0.20/mm or more, particularly 0.25/mm ormore, further 0.3/mm or more, desirably 0.4/mm or more. However, sincethere is a tendency that as the β-OH value grows higher, a strain pointis reduced, it is desired that its upper limit is 0.65/mm or less,particularly 0.6/mm or less. The β-OH value of the glass is obtained bythe following equation in an infrared-ray absorption spectrum of theglass.

β-OH value=(1/X)log 10(T ₁ /T ₂)

X: glass thickness (mm)

T₁: transmittance (%) at a reference wavelength of 3846 cm⁻¹

T₂: minimum transmittance (%) at hydroxy group absorption wavelength ofaround 3600 cm⁻¹

The moisture amount of the glass can be adjusted by a method ofselecting raw materials having a high moisture amount (e.g. hydroxideraw material), or adding moisture to a raw material, or adjusting acontent of a raw material for decreasing a moisture amount in a glasssuch as chlorine, or increasing a moisture amount in the atmosphere in afurnace by adopting oxygen combustion over melting of the glass, orintroducing a water steam directly into a furnace, or performing watersteam bubbling in the molten glass.

In addition, in the glass for a display substrate of the presentinvention, the density is 2.5 g/cm³ or less (preferably 2.45 g/cm³ orless, further preferably 2.42 g/cm³ or less), the average thermalexpansion coefficient in a temperature range of 30 to 380° C. is 25 to36×10⁻⁷/° C. (preferably 28 to 35×10⁻⁷/° C.), and the strain point is640° C. or higher (preferably 650° C. or higher). For this reason,thermal shock resistance is excellent, warpage is not caused due toapproximation to a thermal expansion coefficient of a TFT material,weight reduction is possible, the sag amount can be reduced, and thermalcompaction is small.

In addition, in the glass for a display substrate of the presentinvention, it is desirable that the liquidus temperature is 1150° C. orlower (particularly 1130° C. or lower, further 1100° C. or lower), andthe viscosity at the liquidus temperature is 10^(5.4) dPa·s or more(particularly 10^(6.0) dPa·s or more). By satisfying this condition,even when formed into a sheet by a down-draw process, devitrification isnot caused, and it is possible to decrease a production cost by omittinga polishing step. Further, it is desirable that, when treated in a 10%HCl aqueous solution under condition of 80° C.-24 hours, its erosionamount is 10 μm or less, when treated in a 10% HCl aqueous solutionunder condition of 80° C.-3 hours, cloud or roughness is not recognizedby surface observation with naked eyes, further when treated in a 130BHF solution under condition of 20° C.-30 minutes, its erosion amount is0.8 μm or less and, when treated in a 63 BHF solution under condition of20° C.-30 minutes, cloud or roughness is not recognized by surfaceobservation with naked eyes. In addition, it is desirable that thespecific Young's modulus is 27.5 GPa/g·cm⁻³ or more (particularly 29.0GPa·s or more). By satisfying this condition, the sag amount of theglass substrate can be reduced. Further, when the temperature of theglass melt at the viscosity of 10^(2.5) dPa·s is 1650° C. or lower,meltability becomes better.

In addition, in the glass for a display substrate of the presentinvention, by imparting properties of a low density and a high specificYoung's modulus, reduction in workability is small even when thethickness is 0.6 mm or less (preferably 0.5 mm or less). That is, evenwhen the thickness is reduced from 0.7 mm to 0.6 mm, the sag amountbecomes smaller as compared with the previous glass substrate, and itbecomes easy to prevent damage when the glass substrate is placed intoor taken out from a cassette.

In addition, there is a tendency that a size of a glass substrate isbeing increased and, when the substrate area grows larger, a possibilitythat devitrification appears in the substrate becomes higher, and thegood merchandize rate is rapidly decreased. Therefore, improvement indevitrification has great merits for manufacturing a large-sizedsubstrate glass. A larger size is advantageous, such as the area of 0.1m² or more (specifically, size of 320 mm×420 mm or more), particularly0.5 m² or more (specifically, size of 630 mm×830 mm or more), 1.0 m² ormore (specifically, size of 950 mm×1150 mm or more), further 2.3 m² ormore (specifically, size of 1400 mm×1700 mm or more), 3.5 m² or more(specifically, size of 1750 mm×2050 mm or more), 4.8 m² or more(specifically, size of 2100 mm×2300 mm or more).

Examples of the suitable glass composition for a display substrate ofthe present invention include a glass comprising 50 to 70% of SiO₂, 10to 25% of Al₂O₃, 8.4 to 20% of B₂O₃, 0 to 10% of MgO, 6 to 15% of CaO, 0to 10% of BaO, 0 to 10% of SrO, 0 to 10% of ZnO, 0 to 5% of TiO₂ and 0to 5% of P₂O₅ as expressed in % by mass. This composition was defined inview of properties such as a strain point, a density, a thermalexpansion coefficient, chemical resistance, a specific Young's modulus,meltability and formability which are sought as the aforementionedsubstrate such as a liquid crystal display. The reason why thecomposition range was defined will be explained below.

The content of SiO₂ in the present invention is 50 to 70%. When thecontent is less than 50%, chemical resistance, particularly acidresistance is deteriorated, and it becomes difficult to reduce thedensity. On the other hand, when the content is more than 70%, theviscosity at high temperature becomes high, so that meltability isdeteriorated and, at the same time, a defect of a devitrified substance(cristobalite) is easily produced in the glass. It is preferable thatthe content of SiO₂ is 58% or more, particularly 60% or more, further62% or more, and it is preferable that the content is 68% or less,particularly 66% or less.

The content of Al₂O₃ is 10 to 25%. When the content is less than 10%, itbecomes difficult to adjust the strain point at 640° C. or higher. Inaddition, Al₂O₃ has action of improving the Young's modulus of theglass, and enhancing the specific Young's modulus and, when the contentis less than 10%, the Young's modulus is reduced. On the other hand,when the content is more than 19%, the liquidus temperature is elevated,and devitrification resistance is reduced. It is preferable that thecontent of Al₂O₃ is 10% or more, particularly 12% or more, further 14.5%or more, and it is preferable that the content is 19% or less,particularly 18% or less.

B₂O₃ exerts as a flux, and is an essential component for reducing theviscosity and improving meltability. On the other hand, a glasssubstrate employed in a liquid crystal display is required to have highacid resistance and, as an amount of B₂O₃ grows larger, there is atendency that acid resistance is reduced. The content of B₂O₃ is 8.4 to20%. When the content is less than 8.4%, action as a flux becomesinsufficient and, at the same time, buffered hydrofluoric acidresistance is deteriorated. On the other hand, when the content is morethan 20%, the strain point of the glass is lowered, so that heatresistance is reduced and, at the same time, acid resistance isdeteriorated. Further, since the Young's modulus is reduced, thespecific Young's modulus is reduced. It is preferable that the contentof B₂O₃ is 8.6% or more, additionally 15% or less, particularly 14% orless, further 12% or less.

The content of MgO is 0 to 10%. MgO reduces a viscosity at hightemperature and improves meltability of the glass without lowering thestrain point. In addition, among alkali earth metal oxides, MgO has thegreatest effect of lowering the density. However, when MgO is containedat a large amount, the liquidus temperature is elevated, as a resultdevitrification resistance is reduced. Since MgO has a possibility thatit is reacted with buffered hydrofluoric acid to form a product, theproduct is adhered on an element on the glass substrate surface, and isadhered to the glass substrate to cloud this, its content haslimitation. Therefore, it is desirable that the content of MgO is 0 to2%, preferably 0 to 1%, more preferably 0 to 0.5%, further MgO is notsubstantially contained.

CaO is also a component which reduces a high temperature viscosity andremarkably improves meltability of the glass without lowering the strainpoint, like MgO, and its content is 6 to 15%. This kind of analkali-free glass is generally melted with difficulty. Therefore, inorder to supply a glass substrate of high quality at a low cost and alarge amount, it is important to enhance meltability of the glass. Inthe glass composition of the present invention, reduction in SiO₂ ismost effective for enhancing meltability. However, when the amount ofSiO₂ is reduced, acid resistance is extremely reduced and, at the sametime, the density and the thermal expansion coefficient of the glass areincreased, being not preferable. Therefore, in the present invention, inorder to enhance meltability of the glass, it is preferable that CaO iscontained at 6% or more, particularly 6.5% or more. On the other hand,when the content of CaO is more than 15%, buffered hydrofluoric acidresistance of the glass is deteriorated, so that the glass substratesurface is easily eroded and, at the same time, the reaction product isadhered to the glass substrate surface to cloud the glass and, further,the thermal expansion coefficient becomes too high, being notpreferable. The suitable content of CaO is 12% or less, particularly 10%or less, further 9% or less.

Both of BaO and SrO are a component which improves chemical resistanceand devitrification resistance of the glass, and each of them iscontained at 0 to 10%. However, when these components are contained at alarge amount, the density and the thermal expansion coefficient of theglass are increased. It is preferable that the content of BaO is 5% orless, particularly 2% or less, further 1% or less. It is preferable thatthe content of SrO is 4% or less, particularly 2.7% or less, further1.5% or less.

In addition, BaO and SrO are a component having nature of enhancing,particularly, BHF resistance. Therefore, in order to improve BHFresistance, it is preferable that the total amount of these componentsis 0.1% or more (preferably 0.3% or more, more preferably 0.5% or more).However, since when BaO and SrO are contained too much, the density andthe thermal expansion coefficient of the glass are increased, it isdesirable to suppress the total amount to 6% or less. From a viewpointof enhancement of BHF resistance, it is desirable that the total amountof BaO and SrO is as much as possible in the range. On the other hand,from a viewpoint of reduction in a density and a thermal expansioncoefficient, it is desirable that the total amount is as little aspossible.

ZnO is a component which improves buffered hydrofluoric acid resistanceof the substrate glass and, at the same time, improves meltability. Whencontained at a large amount, the glass is easily devitrified, the strainpoint is lowered, and the density is increased, being not preferable.Therefore, the content is 0 to 7%, preferably 0 to 5%, more preferably3% or less, further preferably 0.9% or less, most preferably 0.5% orless.

Respective components of MgO, CaO, BaO, SrO and ZnO have the effect ofimproving meltability and formability of the glass by remarkablylowering the liquidus temperature of the glass and making it difficultfor a devitrified substance to be produced in the glass, by combinationthereof. However, when the total amount of them is small, action as aflux is not sufficient, so that meltability is deteriorated and, at thesame time, the thermal expansion coefficient is reduced too much, as aresult compatibility of the coefficient with a TFT material is reduced.On the other hand, when the total amount is too much, the density isincreased, and the weight of the glass substrate cannot be reduced and,moreover, the specific Young's modulus is reduced, being not preferable.It is preferable that the total amount of these components is 6 to 20%,particularly 6 to 15%, further 6 to 12%.

TiO₂ is a component which improves chemical resistance, particularlyacid resistance of the glass, and reduces the viscosity at hightemperature to improve meltability, but when it is contained at a largeamount, the glass is colored, and its transmittance is reduced,therefore, the glass is not preferable as a glass substrate for display.Therefore, the content of TiO₂ should be defined at 0 to 5%, preferably0 to 3%, more preferably 0 to 1%.

P₂O₅ is a component which improves devitrification resistance of theglass, but when contained at a large amount, phase separation and cloudoccur in the glass and, at the same time, acid resistance is remarkablydeteriorated, being not preferable. Therefore, the amount of P₂O₅ shouldbe defined at 0 to 5%, preferably 0 to 3%, more preferably 0 to 1%.

In the present invention, in addition to the aforementioned components,various components may be added as far as glass properties are notdeteriorated.

For example, Y₂O₃, Nb₂O₃ and La₂O₃ may be contained at a total amount ofaround 5% or less. These components have action of enhancing the strainpoint and the Young's modulus, but when contained at a large amount, thedensity is increased, being not preferable.

In addition, the glass of the present invention can contain SnO₂ at lessthan 0.3%, particularly not less than 0.005 and less than 0.3, morepreferably 0.01 to 0.28%. In the present invention, SnO₂ is not anessential component, but is a component which can be added as a refiningagent. In addition, when the glass is electrically melted using a SnO₂electrode, SnO₂ which is an electrode component is dissolved out intothe glass. A content of SnO₂ is closely related with devitrification ofthe glass due to ZrO₂ and, as the amount of SnO₂ is larger, the glass iseasily devitrified. This tendency is remarkably manifested,particularly, in the glass, in the aforementioned composition range. Asin the case of ZrO₂, from a viewpoint of improvement in devitrification,the smaller amount of SnO₂ is better. However, SnO₂ is one of a fewrefining agents which exert the refining effect in a high temperatureregion, and high refining effect can be expected at a small amount.Therefore, for the glass of the present invention which is refined withdifficulty due to necessity of high temperature melting, it is desiredthat SnO₂ is contained at 0.005% or more for improving refining propertyand decreasing a use amount of As₂O₃ which is an environmental loadingsubstance. Refining effect of SnO₂ is the same even in the case of SnO₂which has dissolved out from an electrode.

Further, the glass of the present invention may contain As₂O₃, Sb₂O₃,Sb₂O₅, F₂, Cl₂, SO₃, C, Al and Si as a refining agent at a total amountof up to 5%. Alternatively, the glass may contain CeO₂ and Fe₂O₃ as arefining agent at a total amount of up to 5%.

Then, a method for producing a glass for a display substrate of thepresent invention will be explained.

First, glass raw materials are mixed so that the glass having aSiO₂—Al₂O₃—B₂O₃—RO (RO is at least one of MgO, CaO, BaO, SrO and ZnO)based composition and a temperature corresponding to 10^(2.5) poise of1580° C. or higher is obtained, or the glass having a density of 2.5g/cm³ or less, an average thermal expansion coefficient in a temperaturerange of 30 to 380° C. of 25 to 36×10⁻⁷/° C., and a strain point of 640°C. or higher is obtained. It is important that the glass raw materialsare mixed so that an alkali content of the resultant glass is 0.01 to0.2% as expressed in % by mass.

The glass raw materials are desirably mixed so that theSiO₂—Al₂O₃—B₂O₃—RO based glass containing 50 to 70% of SiO₂, 10 to 25%of Al₂O₃, 8.4 to 20% of B₂O₃, 0 to 10% of MgO, 6 to 15% of CaO, 0 to 10%of BaO, 0 to 10% of SrO, 0 to 10% of ZnO, 0 to 5% of TiO₂, and 0 to 5%of P₂O₅ is obtained.

In addition, for the purpose of reducing the viscosity of the glass, itis preferable to select or treat the raw materials so that a largeamount of water is brought into the glass. Specifically, the rawmaterials having a high water content (e.g. hydroxide raw material) maybe selected, or a moisture may be added to the raw materials.

Further, there is a possibility that a content of a ZrO₂ component whichis a cause for devitrification is increased by dissolution out from arefractory at a later melting step. For this reason, it is important toextremely restrict mixing in of the ZrO₂ component from the glass rawmaterials and, also when used aiming at improving chemical durability,it is necessary that its addition amount is restricted to a minimum.

Then, the mixed glass raw materials are melted and vitrified in amelting furnace constructed of a high zirconia refractory. As the highzirconia refractory, it is preferable to use a ZrO₂ electrocastrefractory which is excellent in erosion resistance and can be used fora long term. Alternatively, dense zircon having a short life may be usedin place of the high zirconia refractory. As melting, electric meltingis adopted in which SnO₂ electrodes and Pt electrodes are used alone orin combination of them to directly pass electricity through the glass toheat the glass. It goes without saying that combustion of heavy oil orgas may be used together to melt the glass. In addition, a moistureamount in the atmosphere in the furnace may be increased by using oxygencombustion, or water steam may be introduced directly into the furnace,or water steam bubbling may be performed in a molten glass so that alarge amount of water is introduced into the glass.

Then, the molten glass is refined and homogenized. Although a refiningand homogenizing step may be performed in a vessel made of a refractorysuch as a high zirconia refractory, the step is desirably performed in aplatinum or platinum alloy vessel in order to prevent furtherdissolution out of ZrO₂ into the glass. The platinum vessel means avessel in which a surface contacts with a glass is constructed ofplatinum, for example, a vessel in which a refractory surface is coveredwith platinum or platinum alloy.

Thereafter, the molten glass is formed into a desired shape to obtain asubstrate glass. When used in utility of display, the glass may beformed into a thin sheet using a method such as an overflow down-drawprocess, a slot down-draw process, a float process, and a roll outprocess. In particular, when formed by the overflow down-draw process, aglass sheet very excellent in surface quality is obtained even whenunpolished, being preferable.

In the thus prepared substrate glass of the present invention, itbecomes easy to pass electricity through the glass at electric meltingdue to the presence of an alkali component. For this reason, it does notoccur that the content of ZrO₂ in the glass is excessively increased tointensity devitrification property. In the aforementioned method, it isdesirable that the β-OH value of the resultant glass is adjusted at0.20/mm or more, the content of ZrO₂ is adjusted at not less than 0.01and less than 0.4% (particularly 0.3% or less), and a content of SnO₂ isadjusted at less than 0.3%.

The resultant substrate glass is cut into an appropriate size, subjectedto end face treatment, and is used as a substrate for a liquid crystaldisplay, an EL display or the like.

Example 1

Table 1 shows influence of ZrO₂ on devitrification property of a glass.A glass 1 is a glass containing 60% of SiO₂, 15% of Al₂O₃, 10% of B₂O₃,5% of CaO, 5% of BaO, and 5% of SrO as expressed in % by mass, andhaving a density of 2.5 g/cm³, a thermal expansion coefficient at 30 to380° C. of 37×10⁻⁷/° C., a strain point of 660° C., and a temperaturecorresponding to 10^(2.5) poise of about 1570° C., and a glass 2 is aglass containing 64% of SiO₂, 16% of Al₂O₃, 11% of B₂O₃, 8% of CaO, and1% of SrO, and having a density of 2.4 g/cm³, a thermal expansioncoefficient at 30 to 380° C. of 32×10⁻⁷/° C., a strain point of 675° C.,and a temperature corresponding to 10^(2.5) poise of about 1600° C. Inany glass, an alkali content is less than 0.01%.

TABLE 1 Glass 1 Glass 2 ZrO₂ 0.0 Content 0.1 (% by mass) 0.2 0.3 ≦10000.4 1100 0.5 1110 0.6 ≦1000 1160 0.7 1100 1180 0.8 1140 >1190 0.9 >1180

Each sample was prepared as follows. First, glass raw materials weremixed by changing a ZrO₂ amount so that the aforementioned compositionwas obtained. This raw material batch was put into a platinum crucible,melted at 1600° C. for 24 hours, and the melt was formed. Thereafter,the resultant glass was crushed, passed through a standard sieve of 30mesh (500 μm), the glass powder remaining on 50 mesh (300 μm) was putinto a platinum boat, retained in a temperature gradient furnace for 24hours, and taken out. Regarding the resultant samples, a maximumtemperature at which a ZrO₂.SiO₂ crystal was seen by microscopeobservation is shown.

From the above results, it was confirmed that the glass 2 having a lowdensity, a low expansion, and a high strain point is devitrified at asmaller ZrO₂ amount than that of the glass 1.

Example 2

Tables 2 and 3 show Examples (sample Nos. 2 to 4, and 6 to 8) of a glassfor display of the present invention. Sample Nos. 1 and 5 areComparative Examples.

TABLE 2 1 2 3 4 (% by mass) SiO₂ 64 64 64 64 Al₂O₃ 16 16 16 16 B₂O₃ 1010 10 10 CaO 7 7 7 7 BaO 1 1 1 1 SrO 1 1 1 1 Li₂O 0.0005 0.005 0.0010.007 Na₂O 0.005 0.02 0.05 0.06 K₂O 0.001 0.005 0.01 0.01 ZrO₂ 0.4 0.120.1 0.05 SnO₂ 0.1 0.2 0.05 0.01 As₂O₃ 0.1 0.1 0.1 0.1 Sb₂O₃ 0.9 0.9 0.90.9 Cl₂ 0.1 0.05 — — β-OH Value 0.25 0.30 0.50 0.45 (/mm) Melting 16081605 1600 1603 Temperature (° C.) Density (g/cm³) 2.4 2.4 2.4 2.4Thermal Expansion 38 38 38 38 Coefficient (×10⁻⁷/° C.) Strain Point (°C.) 670 669 665 665 Young's Modulus 71 71 71 71 (GPa) DevitrificationPresence Absence Absence Absence Property

TABLE 3 5 6 7 8 (% by mass) SiO₂ 64 64 64 64 Al₂O₃ 16 16 16 16 B₂O₃ 1010 10 10 CaO 7 7 7 7 BaO 1 1 1 1 SrO 1 1 1 1 Li₂O 0.0006 0.005 0.0010.006 Na₂O 0.006 0.02 0.05 0.05 K₂O 0.001 0.005 0.01 0.01 ZrO₂ 0.4 0.120.1 0.05 SnO₂ 0.2 0.2 0.2 0.2 As₂O₃ 0.7 0.7 0.7 0.7 Sb₂O₃ 0.5 0.5 0.50.5 Cl₂ 0.1 0.05 — — β-OH Value 0.25 0.30 0.50 0.45 (/mm) Melting 16061605 1601 1602 Temperature (° C.) Density (g/cm³) 2.4 2.4 2.4 2.4Thermal Expansion 38 38 38 38 Coefficient (×10⁻⁷/° C.) Strain Point (°C.) 671 669 666 665 Young's Modulus 71 71 71 71 (GPa) DevitrificationPresence Absence Absence Absence Property

Each sample glass in Tables was prepared as follows.

First, glass raw materials such as silica sand, aluminum hydroxide andaluminum oxide, boric acid, calcium carbonate, strontium carbonate,barium carbonate, stannic oxide, soda ash, lithium carbonate, andpotassium carbonate were compounded and mixed so that a composition inTables was obtained. Then, the mixture was melted at a maximumtemperature of 1650° C. by performing direct electricity passing heatingin an electric melting furnace constructed of a ZrO₂ electrocastrefractory and having a SnO₂ electrode. Upon melting, oxygen combustionwas used jointly. Further, the molten glass was introduced into arefractory vessel lined with platinum, and refining and homogenizationwere performed. Subsequently, the molten glass was formed into a sheetby an overflow down-draw process, and cut to obtain a substrate glasshaving a size of 1100×1250×0.7 mm. Regarding glasses, properties such asa 13-OH value, contents of ZrO₂ and SnO₂, and devitrification propertyof the glass were evaluated.

As a result, it was seen that samples No. 2 to 4, and 6 to 8 which areExamples of the present invention are better in devitrificationproperty.

Contents of ZrO₂ and SnO₂ of the resultant glass were confirmed byfluorescent X-ray analysis.

The β-OH value of the glass was obtained using the following equation bymeasuring the glass transmittance using FT-IR.

β-OH value=(1/X)log 10(T ₁ /T ₂)

X: glass thickness (nm)

T₁: transmittance at reference wavelength of 3846 cm⁻¹(%)

T₂: minimum transmittance at hydroxy group absorbing wavelength ofaround 3600 cm⁻¹(%)

A melting temperature (temperature corresponding to 10^(2.5) poise) wasmeasured by a platinum ball pulling up method.

A density was measured by the well-known Archimedes method.

A thermal expansion coefficient was measured with a dilatometer using acylindrical sample formed into a size of a diameter of 5.0 mm and alength of 20 mm, and an average thermal expansion coefficient at 30 to380° C. was obtained from the resultant thermal expansion curve.

A strain point was measured based on a method of ASTM C336-71.

A Young's modulus was obtained by a resonance method.

Regarding devitrification property, a sample which had been processedinto a powder as in Example 1 was put into a platinum boat, this wasretained in a temperature gradient furnace for 24 hours, and taken outtherefrom, thereafter, the presence or the absence of a crystal(devitrifying substance) was observed with a microscope.

The glass for a display substrate of the present invention can be usednot only as a display substrate, but also as a glass substrate materialfor an image sensor of a charge coupling device (CCD), and an equivalentclose-type solid image pickup device (CIS), or for a solar cell.

1. A method for producing a glass for a display substrate comprising thesteps of: preparing glass raw materials mixed so that a glass having aSiO₂—Al₂O₃—B₂O₃—RO based composition, where RO is at least one of MgO,CaO, BaO, SrO and ZnO, and having a melting temperature corresponding to10^(2.5) poise of 1580° C. or higher is obtained; electrically meltingthe glass raw materials in a melting furnace constructed of a highzirconia refractory; and refining, homogenizing and forming the glassmelt; wherein the glass raw materials are mixed so that an alkalicontent of the resultant glass is 0.01 to 0.2% as expressed in % bymass.
 2. A method for producing a glass for a display substratecomprising the steps of: preparing glass raw materials mixed so that aglass having a SiO₂—Al₂O₃—B₂O₃—RO based composition, where RO is atleast one of MgO, CaO, BaO, SrO and ZnO, a density of 2.5 g/cm³ or less,an average thermal coefficient of 25 to 36×10⁻⁷/° C. in a temperaturerange of 30° to 380° C., and a strain point of 640° C. or higher isobtained; electrically melting the glass raw materials in a meltingfurnace constructed of a high zirconia refractory; and refining,homogenizing and forming the glass melt; wherein the glass raw materialsare mixed so that an alkali content of the resultant glass is 0.01 to0.2% as expressed in % by mass.
 3. The method for producing a glass fora display substrate according to claim 1, wherein the glass rawmaterials are mixed so that an alkali component is 0.007 to 0.2% ofNa₂O, 0 to 0.05% of Li₂O, and 0 to 0.05% of K₂O as expressed in % bymass.
 4. The method for producing a glass for a display substrateaccording to claim 1, wherein a β-OH value of the resultant glass is0.20/mm or more.
 5. The method for producing a glass for a displaysubstrate according to claim 1, wherein a ZrO₂ content of the resultantglass is not less than 0.01% and less than 0.4% as expressed in % bymass.
 6. The method for producing a glass for a display substrateaccording to claim 1, wherein the ZrO₂ content of the resultant glass is0.01 to 0.3% as expressed in % by mass.
 7. The method for producing aglass for a display substrate according to claim 1, wherein the rawmaterials are mixed so that the glass contains 50 to 70% SiO₂, 10 to 25%of Al₂O₃, 8.4 to 20% of B₂O₃, 0 to 10% of MgO, 6 to 15% of CaO, 0 to 10%of BaO, 0 to 10% of SrO, 0 to 10% of ZnO, 0 to 5% of TiO₂, and 0 to 5%of P₂O₅ as expressed in % by mass.
 8. A glass for a display substrate,which is produced by the method as defined in claim
 1. 9. The method forproducing a glass for a display substrate according to claim 2, whereinthe glass raw materials are mixed so that an alkali component is 0.007to 0.2% of Na₂O, 0 to 0.05% of Li₂O, and 0 to 0.05% of K₂O as expressedin % by mass.
 10. The method for producing a glass for a displaysubstrate according to claim 2, wherein a β-OH value of the resultantglass is 0.20/mm or more.
 11. The method for producing a glass for adisplay substrate according to claim 2, wherein a ZrO₂ content of theresultant glass is not less than 0.01% and less than 0.4% as expressedin % by mass.
 12. The method for producing a glass for a displaysubstrate according to claim 2, wherein the ZrO₂ content of theresultant glass is 0.01 to 0.3% as expressed in % by mass.
 13. Themethod for producing a glass for a display substrate according to claim2, wherein the raw materials are mixed so that the glass contains 50 to70% SiO₂, 10 to 25% of Al₂O₃, 8.4 to 20% of B₂O₃, 0 to 10% of MgO, 6 to15% of CaO, 0 to 10% of BaO, 0 to 10% of SrO, 0 to 10% of ZnO, 0 to 5%of TiO₂, and 0 to 5% of P2O5 as expressed in % by mass.
 14. A glass fora display substrate, which is produced by the method as defined in claim2.